High Performance Self Leveling Epoxy Flooring
EPOFLOOR SLE50 is a solvent free, high performance three components pigmented self leveling product composed of epoxy resin, hardener, selected silica and color pack. EPOFLOOR SLE50 is used for thickness from 2.5 mm to 5 mm. EPOFLOOR SLE50 has high filling ability when applied to concrete floors. Once cured, it provides a watertight seamless coating with high abrasion, mechanical and chemical resistance.
The product supplied in 15 liter kit.
Consumption: 1.0m²/Liter per 1 mm thickness depending on substrate condition.
Refer to Colmef Color Chart
|Density at 25°C||
1.78 kg /L
|Pot-life time at 25°C||
|Tensile strength (ASTM C 307)||
10 N / mm²
|Compressive strength (ASTM C 579)||
65 N / mm²
|Flexural strength (ASTM C 580)||
35 N / mm²
|Bond strength (ASTM D 4541)||
>2.5 N / mm²
|Abrasion Resistance (ASTM D 4060)||
160 mg/ 1000 cycles
|Open to foot traffic at 25°C||
|Open to vehicular traffic at 25°C||
-5°C to +80°C
All surfaces treated with EPOFLOOR SLE50 should be primed with PRIMER POXY FF, a solvent-free high performance Epoxy primer..
Add the content of Hardener can (Part B) into the Base can (Part A) and mix for two minutes until a homogenous mixture is achieved.
Apply one coat of PRIMER POXY FF onto the dry surface, maintaining the consumption of 150 - 300 g/m² and observing the application intervals indicated in the relative technical data sheet.
Allow Primer to dry before proceeding with the self levelling application. Do not apply EPOFLOOR SLE50 while the primer is tacky as this will lead to unsightly marks in the finished surface.
Highly porous substrates may require a second primer coat.
EPOFLOOR SLE50 is supplied in two pre-weighed packs (Component A – Base and Component B – Hardener) which are ready for immediate in-situ use.
Stir in both components before use. Transfer the entire contents of component B (Hardener) into the component A (Base) can and mix with low speed drill and paddle (200 – 300 rpm) for 2 – 3 minutes till obtaining a mix with uniform consistency. Scrape the sides and bottom of the can during mixing to ensure homogeneity.
Pour the mixed material onto the primed surface in pools or as a long strip. Using a trowel, pin screed, or notched trowel, spread EPOFLOOR SLE50 to the required thickness. To release entrapped air and assist with the smoothing operation, roll the material within 5 minutes after it is leveled, using spiked roller.
Allow to cure for minimum 12 hours at +25°C for light traffic.
Tools and equipment should be cleaned with SOLVENTE 10 immediately after use. Hardened material should be removed mechanically.
Spillages should be absorbed with sand or sawdust and disposed of in accordance with local regulations.
The surface of the concrete to be prepared shall be sound, clean and uncontaminated.
This preparation shall be such as to leave a sound exposed concrete surface free from dust, loose particles and any deleterious matter. If the concrete surface is defective or has laitance, it must be cut back to a sound base. Excess laitance deposits are best removed by light mechanical scrabbling, grinding or grit/captive blasting followed by vacuum cleaning to remove dust debris.
Any blowholes, chipping or similar surface imperfections shall be repaired using EPOFINISH C, a solvent free epoxy resin repair mortar. Allow the repair material to harden.
Expansion joints shall be repaired using EPOMORT HS, a High strength solvent free epoxy mortar.
New concrete or cementitious surfaces should be allowed to cure and have moisture content not exceeding 5%. Old or existing floor should be refurbished mechanically to ensure clear sound substrate.
All metal substrates should be blast cleaned to achieve a minimum of Sa2 ½ standard of roughness, an angular amplitude of at least 75 microns for pedestrian traffic and 100 microns for vehicular traffic. The coating system must be applied over the blasted steel surface immediately. If the standard of the surface falls below Sa2 ½ then the steel must be reblasted.
During application, wear appropriate protective clothing, goggles, gloves and respiratory equipment if necessary.
In case of contact with skin, rinse with water and again wash thoroughly with soap and water. In case of contact with eyes, rinse with plenty of water and seek medical advice accordingly.
If ingested, obtain medical attention immediately. Do not induce vomiting.
The information in this Technical Data Sheet is based on Colmef Monneli’s experience. Colmef Monneli does not accept any liability arising from the use of its products as it has no direct or continuous control over where or how its products are applied. All Colmef Monneli’s Data Sheets are updates on regular basis. It is the user’s responsibility to obtain the latest version.
SOLVENT FREE PERFORMANCE, HIGH BUILD EPOXY FLOORING SYSTEM
Epoxy Floor Coat
High Build Solvent Free Epoxy Flooring System
High Performance Epoxy Floor Coating
Heavy Duty, Anti-Skid Surface Dressing
Elastomeric Single Component Aliphatic Polyurethane Waterproofing Membrane