Industrial Flooring

Polyurethane Based Flooring Systems

Monneli Epofloor P1160

Waterproofing and Protective, Polyurethane Based Traffic Deck Coating System

Uses
EPOFLOOR P1160 can be used as a protective trafficable wear resistant floor coating for variety of applications such as:
Car park decks
Ramps
Mechanical and plant rooms
Trafficable flat roof
Workshops
Factories
Sport stadiums waterproofing coatings
back to Industrial Flooring
Technical Information
Product Description

EPOFLOOR P1160 is a UV stable polyurethane based multi-component car park decking system for exposed and intermediate traffic decks where crack bridging and waterproofing properties are required.

Advantages
  • Excellent abrasion resistance
  • Excellent crack-bridging capacity
  • Excellent UV resistance
  • Even anti-skid finish
  • Formulated to suit Middle East conditions
Packaging, Coverage / Consumption

 

  PACKAGING
   PRIMER PU        15 liter kit    
  EPOFLOOR CF        15 liter pail  
  EPOFLOOR P380       15 liter pail  
  EPOFLOOR P500     15 liter pail  
  EPOFLOOR LM     15 liter pail  
  QUARTZO NO. 2     25 kg bag  
  SOLVENTE 10     20 liter pail  

 

 

  CONSUMPTION
   PRIMER PU    6-8 m²/Liter
depending on surface texture and porosity
  
  EPOFLOOR CF   2.5 m²/Liter at 400 microns DFT  
  EPOFLOOR P 500   3.0 m² / Liter coat (anti-slip)
4.0  m² / Liter/coat (smooth) at 200 microns DFT
 
  EPOFLOOR LM   5.0m²/Liter for 100 micron, (dry) depending on the
surface conditions and method of application
 
  QUARTZO NO. 2   0.6-2.0 kg/m² depending on application  
Shelf Life & Storage

Storage:

Store EPOFLOOR P1160 in dry and covered shed. Exposure to extreme temperature and direct sun light results in the deterioration of the product’s efficiency and reduces its shelf life.

If stored as recommended its shelf life would be 12 months from the manufacturing date.

Technical Properties
PROPERTIES RESULTS
PRIMER PU 
Pot life at 25°C  60 minutes 
Density at 25°C  0.96 kg/L 
Re-coatable time at 25°C 8 - 12 hours
EPOFLOOR CF 
Pot life at 25°C 45 minutes
Mix density at 25°C 1.55 kg/L
Elongation at break > 70%
Tensile strength 6 N / mm²
Shore hardness (A) 60
Initial hardening (dry & touch) 5 hours
Complete hardening 7 days
Application temperature +5ºC to +35ºC
Service resistance –5ºC to +80ºC
EPOFLOOR P380  
Viscosity at 25°C, 50 s-1 800 MPas
Density at 25°C 1.5 kg/L
Elongation Up to 40%
Tensile strength 25 N/mm2
Tear strength 45 N/mm2
Solid content 83%
Open time at 25°C  
Minimum 45 min
Maximum 4 hours
Open to foot traffic at 25°C / 50% RH 6 - 8 hours
Open to vehicular traffic at 25°C / 50% RH 16 hours
EPOFLOOR P500 
Mix density at 25°C 1.3 - 1.4 kg/L
Elongation Approximately 200%
Tensile strength Approximately 4.5N/mm2
Relative atmospheric humidity 40-90%
Application temperature +5°C to +35°C
Water vapor diffusion resistance factor Approximately 3000
Capable of bearing loads After 48 hours
Tack-free After approximately 30 minutes
EPOFLOOR LM 
Solid content 65%
Density at 25°C 1.45 kg/L
Touch dry at 25ºC Approximately 10 minutes
Application temperature 5ºC to 35ºC
Recommend minimum dry film thickness 200 microns
All values are subject to 5-10% tolerance
Application Information
Instructions for use

 

  SYSTEM COMPONENTS  
  PRIMER PU          Solvent based epoxy primer  
    EPOFLOOR CF      Two component tough elastomeric PU coating  
  EPOFLOOR P380      Single component polyurethane protective traffic coating  
  EPOFLOOR P500     Single component polyurethane UV resistant traffic coating  
  EPOFLOOR LM     Line marking coating  

Surface preparation

The surface of the concrete to be prepared shall be sound, clean and uncontaminated.

This preparation shall be such as to leave a sound exposed concrete surface free from dust, loose particles and any deleterious matter. If the concrete surface is defective or has laitance, it must be cut back to a sound base. Excess laitance deposits are best removed by light mechanical scrabbling, grinding or grit/captive blasting followed by vacuum cleaning to remove dust debris.

Any blowholes, chipping or similar surface imperfections shall be repaired using EPOFINISH C, a solvent free epoxy resin repair mortar.

Expansion joints shall be repaired using EPOMORT S, a high strength solvent free epoxy mortar.

New concrete or cementitious surfaces should be allowed to cure and have moisture content not exceeding 5%. Old or existing floor should be refurbished mechanically to ensure clear sound substrate.

Application

Priming

Apply PRIMER PU, a high performance Polyurethane primer using a suitable roller at the rate of 5-6m2/Liter depending on the profile and porosity of the substrate. Allow the applied coat to cure until it is tack free.

The primer should be left to achieve a tack-free condition for 6-8 hours before applying the top coat. If the substrate is excessively porous, a second coat of primer must be applied again.

Intermediate Coat

EPOFLOOR CF is supplied in two pre-weighed packs (Component A – Base and Component B – Hardener) which are ready for immediate in-situ use. Stir in both components before use.

Add the hardener (Part B) to the Base (Part A) container and mix for 20-30 seconds using a heavy duty, slow speed drill fitted with a mixing paddle.

Transfer the mixed material to another pail and again remix for 30 seconds. Pour EPOFLOOR CF onto the primed surface at a rate minimum of 2.5 m²/Liter and spread evenly with a notched trowel. Continuous spiking with a spiked roller should be done to remove all entrapped air. Spiking adjacent layers is recommended at 50% overlaps. Spiking shall stop as soon as the coating starts to set.

While the coating is still wet, broadcast QUARTZO NO.2 at approximately 0.6-2.0 kg/m² (depending on the wearing coat thickness). After 24 hours cure, excess aggregate shall be brushed away.

Protective Traffic Coating

Stir EPOFLOOR P380 properly to ensure uniformity of color before application. Apply by roller or airless spray to the tack-free surface at the minimum rate of 4.0 m2 /Liter per coating.

UV Top Coat

To provide a UV resistant coating to the system and to enhance durability performance, apply one coat of EPOFLOOR P500 at a minimum rate of 4.0 m2/Liter for pedestrian traffic and 3.0 m2/Liter for vehicular traffic by roller or airless spray.

Line Marking Coating

Stir EPOFLOOR LM thoroughly prior to application. It can be applied with brush, roller or airless spray gun at a rate of 5m2/liter (200 microns wet). Dilute the product with 5-10% SOLVENTE 10, if airless spray gun is used. The nozzle tip of the gun should be from 4 to 6 mm. Apply the paint with a pressure of 30-40 psi.

Cleaning

Clean tools with SOLVENTE 10 promptly before material hardens. Cured material must be mechanically removed.

Recommendations

  • EPOFLOOR P1160 should be applied to the prepared floor after a curing of 28 days or more has elapsed.
  • EPOFLOOR P1160 should not be applied to the following substrates: damp substrates, asphalt, PVC tiles or sheets, hardboard / chipboard.
  • Do not apply EPOFLOOR P1160 when the humidity exceeds 90%.
  • Make sure that the substrate temperature is +3°C higher than the dew point.
Additional Information
Health & Safety

Avoid contact with skin & eyes. Protective clothing such as gloves & safety goggles should be worn during application. Treat any splashes to the skin or eyes with fresh water immediately.

Should the product be accidentally swallowed, do not induce vomiting, but call for medical assistance immediately. Ensure adequate ventilation at site and avoid inhalation of vapors.

Important note

The information in this Technical Data Sheet is based on Colmef Monneli’s experience. Colmef Monneli does not accept any liability arising from the use of its products as it has no direct or continuous control over where or how its products are applied. All Colmef Monneli’s Data Sheets are updates on regular basis. It is the user’s responsibility to obtain the latest version.

additional materials
Fast Download
Technical Properties Sheet
download (*.pdf 0.34Mb)
OTHER PRODUCTS
More Products from this section
Monneli Epofloor P1100

Seamless, Flexible, Polyurethane Flooring System

Monneli Epofloor P1140

Seamless, Polyurethane Traffic Deck Coating System

Monneli Epofloor P1150

Protective, Polyurethane Based Traffic Deck Coating System

Monneli Epofloor P1200

Waterproofing and Protective, Polyurethane Based Traffic Deck Coating System

Monneli Epofloor P125

POLYURETHANE COATING FOR CONCRETE FLOORS

view more
RANDOM PRODUCT
Monneli Epofloor SL (IFT)

Solvent-Free Epoxy Self-Leveling Topping (2.0-4.0mm) for Concrete Floors

Uses
EPOFLOOR SL (IFT) has a high gloss finish and is used in various installations such as:
Airport hangars
Commercial and residential car parking
Workshops
Warehousing and storage facilities
Chemical and pharmaceutical factories
Food factories and slaughterhouses
Schools and office buildings
Showrooms
Connected products
Monneli Epofinish C

Fairing Coat Solvent Free Epoxy Mortar

Monneli Epofloor LM

Line Marking Coating for Traffic

Monneli Epofloor P500

Single Component Polyurethane UV Resistant Traffic Coating Low...

Contact us
Choose a location
P.O. Box: 123808, Dubai
Toll: +971 4 8803488
Fax: +971 4 8803450
Site Map